安徽合肥鋁合金犧牲陽極廠家批發(fā)Anhui Hefei aluminum alloy sacrifice anode manufacturers wholesale
Chemical Comb:
Type
Al
Zn%
In%
Cd%
Sn%
Mg%
Ti%
Impurity is not
greater than
Si
Fe
Cu
Al-Zn-In
remainder
2.0-6.0
0.01-0.02
--
--
--
--
0.10
0.15
0.01
Al-Zn-In-Cd
remainder
2.5-4.5
0.018-0.050
0.005-0.020
--
--
--
0.10
0.15
0.01
Al-Zn-In-Sn
remainder
2.2-5.2
0.20-0.045
--
0.018-0.035
--
--
0.10
0.15
0.01
Al-Zn-In-Si
remainder
5.5-7.0
0.025-0.035
--
--
--
--
0.10
0.15
0.01
Al-Zn-In-Sn-Mg
remainder
2.5-4.0
0.020-0.050
--
0.025-0.075
0.50-1.00
--
0.10
0.15
0.01
Al-Zn-In-Mg-Ti
remainder
4.0-7.0
0.020-0.050
--
--
0.50-1.50
0.01-0.08
0.10
0.15
0.01
Electrochemical Property :
Type
Open circuit potential
（-V CSE)
Closed circuit potential
（-V CSE)
Capacitance
A·h/kg
Current efficiency %
Surface dissolving
AL1
1.10-1.18
1.05-1.12
2400min
85min
unibity
AL2
1.10-1.18
1.05-1.12
2600min
90min
unibity
AL3
1.45-1.50
1.40-1.45
2080min
70min
unibity
陽極表面質(zhì)量
1 犧牲陽極的工作表面可為鑄造面。
2 犧牲陽極工作面應(yīng)無氧化渣，毛刺，飛邊，等缺陷，犧牲陽極所有表面允許長度不超過50mm,深度不超過5mm 橫向細裂紋存在，但不允許有裂紋團存在。
3 犧牲陽極工作面允許有鑄造孔，但其深度不得超過陽極厚度的10%，深度不得超出10mm。
4 犧牲陽極工作面應(yīng)保持干凈，不得沾有油漆和油污等。
陽極鐵腳
1 板狀鐵腳
采用鋼筋碳素結(jié)構(gòu)鋼制造。鋼板的成分和尺寸應(yīng)符合 GB／T 700 的規(guī)定。
2 鋼管鐵腳
采用無縫鋼管制造。鋼管成分的尺寸應(yīng)符合 GB／T 17395 的規(guī)定。
3 螺紋鋼鐵腳
采用月牙鋼筋制造。鋼筋的成分，尺寸及外形應(yīng)符合 GB 1499 的規(guī)定。
4 圓鋼鐵腳
采用鋼筋制造。鋼筋的成分和尺寸應(yīng)符合 GB 1499 的規(guī)定。
5 表面處理
鐵腳表面應(yīng)清潔無銹，并經(jīng)鍍鋅或噴砂處理，鍍鋅層質(zhì)量符合 GB/T 3764 的規(guī)定。
6 犧牲陽極與鐵腳之間的接觸電阻
犧牲陽極與鐵腳間的接觸電阻應(yīng)不大于0.001歐姆。
陽極氧化后的鋁或其合金，提高了其硬度和耐磨性，可達250～500千克／平方毫米，良好的耐熱性當(dāng)沒有供電條件或顯現(xiàn)不經(jīng)濟的情況時才有應(yīng)用價值。陰極保護施工，陰極保護原理，陰極保護招標(biāo)適用于土壤中的犧牲陽極材料大多是鎂，在海水中是鋅和鋁。為了使電流輸出盡量保持穩(wěn)定和環(huán)比陽極接地電阻，土壤中的犧牲陽極周邊應(yīng)采用化學(xué)填包料，主要由75%的硫酸鈣，20%的膨潤土和5%硫酸鈉混合而成。犧牲陽極不宜埋放在焦炭中，在成組使用時，陽極間距至少應(yīng)是3m。陽極頂部土壤覆蓋層厚度至少為0.6m。犧牲陽極一般僅經(jīng)濟地應(yīng)用在保護電流需要量小的構(gòu)筑物上和低土壤電阻率環(huán)境中。此外為了能夠測量斷電電位，犧牲陽極應(yīng)通過測量盒與管道相連接，犧牲陽極在交流牽引系統(tǒng)周圍地區(qū)應(yīng)用時，陽極體上的交流感應(yīng)長期電壓不應(yīng)超過20V。陰極保護施工，陰極保護原理，陰極保護招標(biāo)陽極要求：陰極保護施工，陰極保護原理，犧牲陰極保護陽極。